Microstructural evaluation and mechanical properties of bulk nanostructured Al86Cu6Y6La2 (at.%) alloy produced by hot consolidation of amorphous melt-spun flakes

توسط میلاد داداشی

Microstructural evaluation and mechanical properties of bulk nanostructured Al86Cu6Y6La2 (at.%) alloy produced by hot consolidation of amorphous melt-spun flakes

Title:Microstructural evaluation and mechanical properties of bulk nanostructured Al86Cu6Y6La2 (at.%) alloy produced by hot consolidation of amorphous melt-spun flakes
 
 
 
 
Author(s):

Dadashi, M., Salehi, M., Shabestari, S.G.

Published/Type:2023 (2023-1-15) / Original Article
Journal:Journal of Non Crystalline Solids600:-

Abstract:

 
 
Altmetrics 
Amorphous melt- spun Al86Cu6Y6La2 (at.%) alloy is hot consolidated at T = 723 K and P = 700 MPa. The glassy ribbons show three devitrification steps which fcc-Al phase is precipitated during the first crystallization stage, and formation of intermetallic compounds (Al3Y, AlCu, AlCu3 and Al3Y5) take place in the next steps. The calculated Avrami exponent (n ∼ 2.6) shows the first crystallization reaction…

View at:

Scopus

یک پاسخ بگذارید

نشانی ایمیل شما منتشر نخواهد شد. بخش‌های موردنیاز علامت‌گذاری شده‌اند *

تماس با ما
لطفاً فرم زیر را پر کنید تا بتوانید مستقیماً با من گفتگو کنید.

    ۳۴+ سایت از پیش ساخته شده